ASTM B807/B807M-20
Standard Practice for Extrusion Press Solution Heat Treatment for Aluminum Alloys
1.1 This practice establishes the controls required for extrusion press solution heat treatment of the 6xxx and 7xxx series aluminum alloys in Table 1 when ASTM material specifications allow use of this process in lieu of furnace solution heat treatment. For the alloys listed in Table 1, this practice is an alternate process to solution heat treatment in a furnace, such as specified in Practice B918/B918M for the attainment of T3, T4, T6, T7, T8, and T9-type tempers (see ANSI H35.1/H35.1M).
1.2 This practice applies only to extrusion press solution heat treatment for aluminum alloys. Precipitation hardening (aging) and annealing processing and equipment calibration shall meet the practice and requirements of Practice B918/B918M.
1.3 The values stated in either Metric SI units or US Customary units are to be regarded separately as standard. The Metric SI units are shown in brackets or in separate tables. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.