DIN EN ISO 10893-5:2011

Non-destructive testing of steel tubes - Part 5: Magnetic particle inspection of seamless and welded ferromagnetic steel tubes for the detection of surface imperfections (ISO 10893-5:2011); German version EN ISO 10893-5:2011

This part of ISO 10893 specifies requirements for magnetic particle inspection of seamless and welded ferromagnetic steel tubes for the detection of surface imperfections on the tube body and the end/bevel face at the ends.*The DIN EN ISO 10893-1 to -12 standard series summarizes the non-destructive tests (abbreviated NDT) for steel tubes. This standard series replaces the previous DIN EN 10264-1 to -18 standard series. The consensus reached at an international level on carrying out non-destructive testing on steel tubes is another step towards worldwide harmonization on the international pipe market. Non-destructive tests represent, in addition to destructive mechanical tests, the most important elements of quality assurance for steel tubes. They are widely used, often during production, for quality assurance. Non-destructive tests are primarily used on pressure-retaining pipes for chemical, petrochemical and power station industries. They can also be agreed on with regard to tests of parts of the body (limited to the weld seam or pipe ends) or with regard to testing the whole body. The most important methods are electromagnetic testing (see Parts 1 to 3), radiographic testing (see Parts 6 and 7), and ultrasonic testing (see Parts 8 to 12). Ultrasonic testing is the usual test method for all tube thicknesses and tube diameters; it is the preferred test method especially for thick-walled tubes. Increased test speeds can be achieved with the electromagnetic methods (eddy current method and magnetic leakage-flux method) where the eddy current method is limited to pipes with smaller diameters and the magnetic leakage-flux method to ferromagnetic pipes. Radiographic testing of weld seams with X-rays has been established for testing safety-relevant tubes (for example, in nuclear technology). In addition to the three standardized methods, dye penetration testing (see Part 4) and the magnetic particle inspection (see Part 5), which are used to detect surface imperfections shall be mentioned. After agreement, the non-destructive tests of EN ISO 10893 can be carried out on hollow sections which are used in steel construction. The Iron and Steel Standards Committee (FES), Subcommittee NA 021-00-09-06 UA "Zerstörungsfreie Prüfung von Rohren" ("Non-destructive testing of pipes") is responsible for this standard series.

Deutsches Institut für Normung [din]

Document History
We have no document history for this standard.
Included in Packages
This standard is not included in any packages.
Amendments & Corrections
We have no amendments or corrections for this standard.