ASTM G28-22

Standard Test Methods for Detecting Susceptibility to Intergranular Corrosion in Wrought, Nickel-Rich, Chromium-Bearing Alloys


1.1These test methods cover two tests as follows:

1.1.1Method A, Ferric Sulfate-Sulfuric Acid Test (Sections 3 "“ 10, inclusive) - This test method describes the procedure for conducting the boiling ferric sulfate - 50 % sulfuric acid test which measures the susceptibility of certain nickel-rich, chromium-bearing alloys to intergranular corrosion (see Terminology G193), which may be encountered in certain service environments. The uniform corrosion rate obtained by this test method, which is a function of minor variations in alloy composition, may easily mask the intergranular corrosion components of the overall corrosion rate on alloys N10276, N06022, N06059, and N06455.

1.1.2Method B, Mixed Acid-Oxidizing Salt Test (Sections 11 "“ 18, inclusive) - This test method describes the procedure for conducting a boiling 23 % sulfuric + 1.2 % hydrochloric + 1 % ferric chloride + 1 % cupric chloride test which measures the susceptibility of certain nickel-rich, chromium-bearing alloys to display a step function increase in corrosion rate when there are high levels of grain boundary precipitation.

1.2The purpose of these two test methods is to detect susceptibility to intergranular corrosion as influenced by variations in processing or composition, or both. Materials shown to be susceptible may or may not be intergranularly corroded in other environments. This must be established independently by specific tests or by service experience.

1.3The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.

1.3.1Exception - Some desired corrosion rate units in 8.1.1 are given in inch-pound units.

1.4This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Warning statements are given in 5.1.1, 5.1.3, 5.1.9, 13.1.1, and 13.1.11.

1.5This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.


CONTENT PROVIDER
ASTM International [astm]

Others Also Bought
Standard Test Method for Microindentation Hardness of Materials
Standard Test Method for Analysis of Nickel Alloys by Spark Atomic Emission Spectrometry
Standard Terminology Relating to Metallography
Included in Packages
This standard is not included in any packages.
Document History
Amendments & Corrections
We have no amendments or corrections for this standard.